Registro completo de metadados
Campo DCValorIdioma
dc.creatorMedeiros, Fabiana Kelly de-
dc.date.accessioned2023-01-23T15:09:28Z-
dc.date.available2022-02-28-
dc.date.available2023-01-23T15:09:28Z-
dc.date.issued2021-07-28-
dc.identifier.urihttps://repositorio.ufpb.br/jspui/handle/123456789/25912-
dc.description.abstractIn the present work, the influence of simultaneous Ti and B doping on the thermomechanical, structural and magnetic properties of Heusler CuAlMn alloys was investigated. The samples were prepared by induction casting and characterized by X-Ray Diffraction (XRD), Differential Thermal Analysis (DTA), Optical Microscopy (OM), Scanning Electron Microscopy (SEM), microhardness and magnetometry tests. The alloys presented the austenitic phase with L21 + DO3 structures. It was found that TiB doping reduced the average grain size and increased the amount of second-phase precipitates, which was attributed to the low solubility of Ti in the austenitic matrix. A reduction in Curie temperature, melting temperature, melting enthalpy and HV microhardness values was observed with TiB doping for the ternary CuMnAl system. It was also verified that the simultaneous doping of Ti and B changed the magnetic behavior of the CuAlMn system from paramagnetic (with weak ferromagnetic contribution) to ferromagnetic. Our results bring to light a new alternative for doping CuAlMn alloy, which, in addition to improving the structural and magnetic properties, presents interesting parameters for technological applications.pt_BR
dc.description.provenanceSubmitted by Fernando Augusto Alves Vieira (fernandovieira@biblioteca.ufpb.br) on 2023-01-10T10:16:37Z No. of bitstreams: 2 license_rdf: 805 bytes, checksum: c4c98de35c20c53220c07884f4def27c (MD5) FabianaKellydeMedeiros_Tese.pdf: 4466781 bytes, checksum: 99dbc50f3007863479e91201b9d14754 (MD5)en
dc.description.provenanceApproved for entry into archive by Biblioteca Digital de Teses e Dissertações BDTD (bdtd@biblioteca.ufpb.br) on 2023-01-23T15:09:28Z (GMT) No. of bitstreams: 2 license_rdf: 805 bytes, checksum: c4c98de35c20c53220c07884f4def27c (MD5) FabianaKellydeMedeiros_Tese.pdf: 4466781 bytes, checksum: 99dbc50f3007863479e91201b9d14754 (MD5)en
dc.description.provenanceMade available in DSpace on 2023-01-23T15:09:28Z (GMT). No. of bitstreams: 2 license_rdf: 805 bytes, checksum: c4c98de35c20c53220c07884f4def27c (MD5) FabianaKellydeMedeiros_Tese.pdf: 4466781 bytes, checksum: 99dbc50f3007863479e91201b9d14754 (MD5) Previous issue date: 2021-07-28en
dc.description.sponsorshipConselho Nacional de Pesquisa e Desenvolvimento Científico e Tecnológico - CNPqpt_BR
dc.languageporpt_BR
dc.publisherUniversidade Federal da Paraíbapt_BR
dc.rightsAcesso abertopt_BR
dc.rightsAttribution-NoDerivs 3.0 Brazil*
dc.rights.urihttp://creativecommons.org/licenses/by-nd/3.0/br/*
dc.subjectEngenharia Mecânicapt_BR
dc.subjectLigas CuAlMnpt_BR
dc.subjectDopagempt_BR
dc.subjectFerromagnéticopt_BR
dc.subjectPropriedades estruturais e magnéticaspt_BR
dc.subjectMechanical Engineeringpt_BR
dc.subjectCuAlMn alloyspt_BR
dc.subjectDopingpt_BR
dc.subjectFerromagneticpt_BR
dc.subjectStructural and magnetic propertiespt_BR
dc.subjectDopagem simultânea com Ti e Bpt_BR
dc.subjectSimultaneous doping with Ti and Bpt_BR
dc.titleInfluência da adição simultânea de TiB nas propriedades térmicas, magnéticas e microestruturais de uma liga CuAlMnpt_BR
dc.typeTesept_BR
dc.contributor.advisor1Gomes, Rodinei Medeiros-
dc.contributor.advisor1Latteshttp://lattes.cnpq.br/2571715314037365pt_BR
dc.contributor.advisor-co1Oliveira, Danniel Ferreira de-
dc.contributor.advisor-co1Latteshttp://lattes.cnpq.br/3903255880120747pt_BR
dc.creator.Latteshttp://lattes.cnpq.br/3979635653607102pt_BR
dc.description.resumoNo presente trabalho foi investigada a influência da dopagem simultânea do Ti e B nas propriedades termomecânicas, estruturais e magnéticas de ligas Heusler CuAlMn. As amostras foram preparadas por fundição por indução e caracterizadas por Difração de Raios X (DRX), Análise Térmica Diferencial (DTA), Microscopia Ótica (MO), Microscopia Eletrônica de Varredura (MEV), ensaios de microdureza e de magnetometria. As ligas apresentaram a fase austenítica com estruturas L21 + DO3. Verificou-se que a dopagem de TiB reduziu o tamanho médio de grão e aumentou a quantidade de precipitados de segunda fase, o que foi atribuído à baixa solubilidade do Ti na matriz austenítica. Observou-se redução nos valores de temperatura Curie, temperatura de fusão, entalpia de fusão e microdureza HV com a dopagem de TiB para o sistema ternário CuMnAl. Verificou-se também que a dopagem simultânea de Ti e B alterou o comportamento magnético do sistema CuAlMn de paramagnético (com fraca contribuição ferromagnética) para ferromagnético. Nossos resultados trazem à tona uma nova alternativa para dopagem da liga CuAlMn, onde além de melhorar as propriedades estruturais e magnéticas, apresenta parâmetros interessantes para aplicações tecnológicas.pt_BR
dc.publisher.countryBrasilpt_BR
dc.publisher.departmentEngenharia Mecânicapt_BR
dc.publisher.programPrograma de Pós-Graduação em Engenharia Mecânicapt_BR
dc.publisher.initialsUFPBpt_BR
dc.subject.cnpqCNPQ::ENGENHARIAS::ENGENHARIA MECANICApt_BR
Aparece nas coleções:Centro de Tecnologia (CT) - Programa de Pós-Graduação em Engenharia Mecânica

Arquivos associados a este item:
Arquivo Descrição TamanhoFormato 
FabianaKellydeMedeiros_Tese.pdf4,36 MBAdobe PDFVisualizar/Abrir
Mostrar registro simples do item Visualizar estatísticas