dc.creatorFigueiredo, Diego Vieira-
dc.date.accessioned2025-07-11T12:29:09Z-
dc.date.available2024-09-11-
dc.date.available2025-07-11T12:29:09Z-
dc.date.issued2024-06-28-
dc.identifier.urihttps://repositorio.ufpb.br/jspui/handle/123456789/35151-
dc.description.abstractThe overall objective of this work is to investigate the production of calcium ferrite through three different synthesis methods: Sol-gel (SG), Solution Blow Spinning (SBS), and High Energy Milling (HEM), and to evaluate which method results in the best oxygen evolution reaction (OER). The specific objectives include the synthesis of ferrites with the stoichiometry of CaFe2O4 using the solgel proteic technique, Solution Blow Spinning (SBS), and High Energy Milling (HEM). The microstructure was analyzed using X-ray diffraction (XRD), infrared spectroscopy (FTIR), Raman spectroscopy, Mössbauer spectroscopy and X-ray photoelectron spectroscopy (XPS). The electrochemical nature of the samples was characterized through linear sweep voltammetry (LSV), cyclic voltammetry (CV), and electrochemical impedance spectroscopy (EIS). It was observed that the morphology of CaFe2O4 produced via SBS exhibited the best catalytic response for OER compared to the SG and HEM morphologies, achieving current density generation performance at 10 mA cm-2 with an overpotential (η) of 300 mV, a Tafel slope of 41 mV dec-1, and specific activity (SA) of 10.56 mA cm-2.pt_BR
dc.description.provenanceSubmitted by Jackson R. L. A. Nunes (jackson@biblioteca.ufpb.br) on 2025-07-11T12:29:09Z No. of bitstreams: 2 license_rdf: 805 bytes, checksum: c4c98de35c20c53220c07884f4def27c (MD5) DiegoVieiraFigueiredo_Dissert.pdf: 3605857 bytes, checksum: 5cf34e7268d2a90675a73bc5c3e3bcf5 (MD5)en
dc.description.provenanceMade available in DSpace on 2025-07-11T12:29:09Z (GMT). No. of bitstreams: 2 license_rdf: 805 bytes, checksum: c4c98de35c20c53220c07884f4def27c (MD5) DiegoVieiraFigueiredo_Dissert.pdf: 3605857 bytes, checksum: 5cf34e7268d2a90675a73bc5c3e3bcf5 (MD5) Previous issue date: 2024-06-28en
dc.description.sponsorshipCoordenação de Aperfeiçoamento de Pessoal de Nível Superior - CAPESpt_BR
dc.languageporpt_BR
dc.publisherUniversidade Federal da Paraíbapt_BR
dc.rightsAcesso abertopt_BR
dc.rightsAttribution-NoDerivs 3.0 Brazil*
dc.rights.urihttp://creativecommons.org/licenses/by-nd/3.0/br/*
dc.subjectEngenharia de materiaispt_BR
dc.subjectFerritas de Cálciopt_BR
dc.subjectEvolução e Reação de Oxigêniopt_BR
dc.subjectSolution Blow Spinningpt_BR
dc.subjectMoagem de alta energiapt_BR
dc.subjectSol-Gelpt_BR
dc.subjectCalcium Ferrites (CaFe2O4)pt_BR
dc.subjectOxygen Evolution Reaction (OER)pt_BR
dc.subjectHigh Energy Milling (HEM)pt_BR
dc.titleFerrita de cálcio ortorrômbica : impacto da metodologia de síntese nas características microestruturais e eletroquímicaspt_BR
dc.typeDissertaçãopt_BR
dc.contributor.advisor1Macedo, Daniel Araújo de-
dc.contributor.advisor1Latteshttp://lattes.cnpq.br/1027496814443777pt_BR
dc.contributor.advisor-co1Raimundo, Rafael Alexandre-
dc.contributor.advisor-co1Latteshttp://lattes.cnpq.br/9772819884310876pt_BR
dc.creator.Latteshttp://lattes.cnpq.br/1087591510238183pt_BR
dc.description.resumoO objetivo geral deste trabalho é investigar a produção de ferrita de cálcio através de três diferentes métodos de síntese: Sol-gel (SG), Solution Blow Spinning (SBS) e Moagem (HEM) e avaliar em qual deles ocorre a melhor reação de evolução de oxigênio (OER). Os objetivos específicos incluem a síntese de ferritas com estequiometria do tipo CaFe2O4 utilizando as técnicas sol-gel proteico, Fiação por solução (solution blow spinning, SBS) e Moagem de alta energia (high energy miling, HEM). A microestrutura foi analisada por meio das técnicas de difração de raios X (DRX), espectroscopia de infravermelho (FTIR) e Raman, Espectroscopia de Mössbauer além de Espectroscopia de Fotoelétrons de Raios X (XPS). A caracterização da natureza eletroquímica das amostras por meio das técnicas de Voltametria de Varredura Linear (LSV), Voltametria Cíclica (CV) e Espectroscopia de Impedância Eletroquímica (EIS). Observou-se que a morfologia da CaFe2O4 via SBS apresentou melhor resposta catalítica para OER em comparação às morfologias SG e HEM, alcançando uma performance de geração de densidades de corrente para 10mA cm-2 com sobrepotencial (η) de 300 mV, inclinação tafel de 41 mV dec-1 e atividade específica (SA) de 10,56 mA cm-2.pt_BR
dc.publisher.countryBrasilpt_BR
dc.publisher.departmentEngenharia de Materiaispt_BR
dc.publisher.programPrograma de Pós-Graduação em Ciência e Engenharia de Materiaispt_BR
dc.publisher.initialsUFPBpt_BR
dc.subject.cnpqCNPQ::ENGENHARIASpt_BR
Aparece nas coleções:Centro de Tecnologia (CT) - Programa de Pós-Graduação em Ciência e Engenharia de Materiais

Arquivos associados a este item:
Arquivo Descrição TamanhoFormato 
DiegoVieiraFigueiredo_Dissert.pdf3,52 MBAdobe PDFVisualizar/Abrir


Este item está licenciada sob uma Licença Creative Commons Creative Commons