dc.creatorNascimento, Elaine Cristina Henrique do-
dc.date.accessioned2022-09-28T21:15:59Z-
dc.date.available2022-08-18-
dc.date.available2022-09-28T21:15:59Z-
dc.date.issued2021-02-24-
dc.identifier.urihttps://repositorio.ufpb.br/jspui/handle/123456789/24803-
dc.description.abstractWith the development of new multicomponent alloys aimed at improving mechanical properties, the use of recycled aluminum to produce new alloys is becoming a new alternative for the industrial market, in addition to contributing to the reuse of these materials have low cost. Furthermore, to improve the mechanical properties it is necessary to understand the microstructural behavior of the alloys. In view of this, this work aimed to understand the effects of the addition of Si and of a quasicrystalline material (Al 25,5Cu-12Fe) in the microstructural variation of recycled aluminum, as well as its effects on the liquidus isotherm velocity (VL) and the cooling rate (TR) solidified under pressure. Recycled aluminum alloys (Alrec) with the addition of 5%Si and 5%Quasicrystal were produced in a cylindrical mold under 100Mpa pressure with a pressing time of 10 seconds. It was observed that the addition of the elements (Si and Quasicrystal) promoted an increase in the values of the thermal parameters (VL, TR) compared to the recycled Al alloy, i.e., addition of the elements facilitated heat extraction, providing a faster solidification. Differences in the microstructures of the alloys were identified: the recycled Al alloy showed a cellular morphology, however for Alrec-5%Si e Alrec 5%Quasicrystal alloys the microstructure was predominantly dendritic throughout the ingot. Microstructural spacings (λc and λ2) were also observed to decrease with increasing liquidus isotherm displacement velocity and cooling rate. Moreover, in Alrec 5%Quasicrystal alloy it was noted the presence of intermetallics in the central region of the ingot, for being a multicomponent alloy, the formation of intermetallics is directly related to the thermodynamic conditions to the solute interdiffusion, in the initial instants of solidification.pt_BR
dc.description.provenanceSubmitted by Fernando Augusto Alves Vieira (fernandovieira@biblioteca.ufpb.br) on 2022-09-28T10:17:59Z No. of bitstreams: 2 license_rdf: 805 bytes, checksum: c4c98de35c20c53220c07884f4def27c (MD5) ElaineCristinaHenriqueDoNascimento_Dissert.pdf: 3946593 bytes, checksum: 9b284d73f20f68bc6c756c2ce74f47bf (MD5)en
dc.description.provenanceApproved for entry into archive by Biblioteca Digital de Teses e Dissertações BDTD (bdtd@biblioteca.ufpb.br) on 2022-09-28T21:15:59Z (GMT) No. of bitstreams: 2 license_rdf: 805 bytes, checksum: c4c98de35c20c53220c07884f4def27c (MD5) ElaineCristinaHenriqueDoNascimento_Dissert.pdf: 3946593 bytes, checksum: 9b284d73f20f68bc6c756c2ce74f47bf (MD5)en
dc.description.provenanceMade available in DSpace on 2022-09-28T21:15:59Z (GMT). No. of bitstreams: 2 license_rdf: 805 bytes, checksum: c4c98de35c20c53220c07884f4def27c (MD5) ElaineCristinaHenriqueDoNascimento_Dissert.pdf: 3946593 bytes, checksum: 9b284d73f20f68bc6c756c2ce74f47bf (MD5) Previous issue date: 2021-02-24en
dc.description.sponsorshipCoordenação de Aperfeiçoamento de Pessoal de Nível Superior - CAPESpt_BR
dc.languageporpt_BR
dc.publisherUniversidade Federal da Paraíbapt_BR
dc.rightsAcesso embargadopt_BR
dc.rightsAttribution-NoDerivs 3.0 Brazil*
dc.rights.urihttp://creativecommons.org/licenses/by-nd/3.0/br/*
dc.subjectAlumínio recicladopt_BR
dc.subjectSolidificação sob pressãopt_BR
dc.subjectParâmetros térmicospt_BR
dc.subjectMicroestruturapt_BR
dc.subjectRecycled aluminumpt_BR
dc.subjectSolidification under pressurept_BR
dc.subjectThermal parameterspt_BR
dc.subjectMicrostructurept_BR
dc.titleInfluência do Si e quasicristal (Al-25,5Cu-12 Fe) na microestrutura de ligas de aluminio reciclado solidificados sob pressãopt_BR
dc.typeDissertaçãopt_BR
dc.contributor.advisor1Torres, Sandro Marden-
dc.contributor.advisor1Latteshttp://lattes.cnpq.br/1050045022082025pt_BR
dc.contributor.advisor-co1Siqueira Filho, Cláudio Alves de-
dc.contributor.advisor-co1Latteshttp://lattes.cnpq.br/3163231207672113pt_BR
dc.creator.Latteshttp://lattes.cnpq.br/4072681419120210pt_BR
dc.description.resumoCom o desenvolvimento de novas ligas multicomponentes visando melhorias nas propriedades mecânicas, o uso de alumínio reciclado para produzir novas ligas vai se tornando uma nova alternativa para o mercado industrial, além de contribuir para o reaproveitamento desses materiais apresentam baixo custo. Além disso, para o melhoramento das propriedades mecânicas se faz necessário entender o comportamento microestrutural das ligas. Diante disto, este trabalho buscou compreender os efeitos da adição do Si e de um material quasicristalino (Al-25,5Cu-12Fe) na variação microestrutural do alumínio reciclado, bem como seus efeitos na velocidade da isoterma liquidus (VL) e na taxa de resfriamento (TR) solidificado sob pressão. Foram produzidas ligas de Alumínio reciclado (AlRec) com a adição de 5% Si e 5%Quasicristal, em molde cilíndrico sob pressão de 100Mpa com tempo de prensagem de 10 segundos. Observou se que a adição dos elementos (Si e Quasicristal) promoveu um aumento nos valores dos parâmetros térmicos (VL, TR) comparado com a liga de Al reciclado, ou seja, adição dos elementos facilitou a extração de calor, proporcionado uma solidificação mais rápida. Identificaram-se diferenças das microestruturas das ligas: a liga de Al reciclado apresentou uma morfologia celular, entretanto para as ligas Alrec-5%Si e Alrec 5%Quasicristal a microestrutura predominantemente foi a dendrítica ao longo de todo lingote. Observou-se também os espaçamentos microestrututais (λc e λ2) diminuem com o aumento da velocidade de deslocamento da isoterma liquidus e da taxa de resfriamento. Além disso, na liga Alrec-5%Quasicristal notou-se a presença de intermetálicos na região central do lingote, por ser uma liga multicomponentes, a formação de intermetálicos está diretamente relacionado com as condições termodinâmicas à interdifusão de soluto, nos instantes iniciais da solidificação.pt_BR
dc.publisher.countryBrasilpt_BR
dc.publisher.departmentEngenharia Mecânicapt_BR
dc.publisher.programPrograma de Pós-Graduação em Engenharia Mecânicapt_BR
dc.publisher.initialsUFPBpt_BR
dc.subject.cnpqCNPQ::ENGENHARIAS::ENGENHARIA MECANICApt_BR
Aparece nas coleções:Centro de Tecnologia (CT) - Programa de Pós-Graduação em Engenharia Mecânica

Arquivos associados a este item:
Arquivo Descrição TamanhoFormato 
ElaineCristinaHenriqueDoNascimento_Dissert.pdf3,85 MBAdobe PDFVisualizar/Abrir
ElaineCristinaHenriqueDoNascimento_Dissert_Ficha_SIGAA.pdf2,1 kBAdobe PDFVisualizar/Abrir


Este item está licenciada sob uma Licença Creative Commons Creative Commons